Alumina (Al 2O 3) is a widely used material for catalysis in the chemical industry. Besides a high specific surface area, acid sites on Al 2O 3 play a crucial role in the chemical transformation of adsorbed molecules, which ultimately react and desorb from the catalyst. This study introduces a synthetic method based on electrospinning to produce Al 2O 3 nanofibers (ANFs) with acidity and porosity tuned using different aluminum precursor formulations. After electrospinning and heat treatment, the nanofibers form a non-woven network with macropores (∼4 μm). Nanofibers produced from aluminum di(sec-butoxide)acetoacetic ester chelate (ASB) show the highest total acidity of ca. 0.70 µmol/m 2 determined with temperature-programmed desorption of ammonia (NH 3-TPD) and BET. The nature of the acid site in ASB ANFs is studied in detail with infrared (IR) spectroscopy. Pyridine is used as a molecular probe for the identification of acid sites in ASB. Pyridine showed the presence of Lewis acid sites prominently. Density-functional theory (DFT) is conducted to understand the desorption kinetics of the adsorbed chemical species, such as ammonia (NH 3) on crystalline γ-Al 2O 3. For our analysis, we focused on a mobile approach for chemisorbed and physisorbed NH 3. The computational results are compared with NH 3-TPD experiments, ultimately utilized to estimate the desorption energy and kinetic desorption parameters. The experiments are found to pair up with our simulation results. We predict that these non-woven structures will find application as a dispersion medium of metallic particles in catalysis.
- NH -TPD
- Porous Alumina