Spatial variability in the mechanical properties of Gilsocarbon

Jose Arregui-Mena, William Bodel, Robert Worth, Lee Margetts, Paul Mummery

    Research output: Contribution to journalArticlepeer-review

    619 Downloads (Pure)

    Abstract

    The objective of this study is to investigate whether there is significant spatial variability in the mechanical properties of Gilsocarbon nuclear graphite at different sections of the billet; specifically the dynamic Poisson’s ratio, dynamic shear modulus, dynamic Young’s modulus and density. Similar studies have been done, usually in the context of manufacturing, to assess the quality of graphite components for nuclear reactors. In this new study, the measurements have been carried out at a much higher spatial resolution than previously. A Torness/Heysham B billet was machined into cubes so that measurements could be made across the circumference and height of the billet. ASTM standards were followed to assess the measurements of the samples. The spatial variability of material properties is described and analysed statistically. The study shows that material variability is present at different heights and circumferential locations of the billet. This discovery will have a significant impact on the structural integrity and through life performance predictions made in industry; both in current and future nuclear reactors. The computer modelling of graphite components may predict different outcomes to standard analyses (that use mean values) if this variability is incorporated into the analysis workflow; specifically through stochastic modelling.
    Original languageEnglish
    Pages (from-to)497-517
    Number of pages20
    JournalCarbon
    Volume110
    Early online date22 Sept 2016
    DOIs
    Publication statusPublished - 1 Dec 2016

    Keywords

    • Carbon
    • Gilsocarbon
    • Nuclear Energy
    • Mechanical properties

    Research Beacons, Institutes and Platforms

    • Energy

    Fingerprint

    Dive into the research topics of 'Spatial variability in the mechanical properties of Gilsocarbon'. Together they form a unique fingerprint.

    Cite this