Synthesis and characterisation of sterically stabilised polypyrrole particles using a chemically reactive poly(vinyl amine)-based stabiliser

Poly(vinyl amine) (PVAm) was derivatised using 2-thiophenecarboxaldehyde via Michael addition to prepare a statistical copolymer stabiliser for the synthesis of primary amine-functionalised polypyrrole (PPy) particles. A minimum stabiliser concentration of around 20 % (w/v) relative to pyrrole was required for well-defined PPy particles of approximately 100-200 nm, as judged by transmission electron microscopy (TEM) and dynamic light scattering (DLS). FTIR spectroscopy confirmed that stabiliser grafting had occurred, while x-ray photoelectron spectroscopy (XPS) studies indicated a stabiliser surface coverage on the PPy particles of around 53 %. PPy particles prepared at stabiliser concentrations below 20 % (w/v) were not colloidally stable above pH 6. However, higher stabiliser concentrations (e.g., 50 % (w/v) based on pyrrole) led to a significant improvement, with colloidal stability being retained above pH 7. Long-term colloidal stability studies of PPy particles stored at pH 7.5 confirmed that the amine-based stabiliser produced more stable aqueous dispersions than the imine-based stabiliser, since the latter bond is hydrolytically unstable.