The effect of reinforcement with woven E-glass fibers on the impact strength of complete dentures fabricated with high-impact acrylic resin

Sung Hun Kim, David C. Watts

    Research output: Contribution to journalArticlepeer-review

    Abstract

    Statement of problem The fracture of acrylic maxillary complete dentures occurs frequently during service through heavy occlusal force or accidental damage. Purpose The purposes of this study were to measure the impact strength of maxillary complete dentures fabricated with high-impact acrylic resin and to evaluate the effect of woven E-glass fiber-reinforcement on the impact strength of the complete dentures. Material and methods Preimpregnated woven E-glass fibers (Stick Net) were used to reinforce 10 complete denture bases fabricated with a heat-polymerized high-impact acrylic resin (Lucitone 199). Ten unreinforced complete dentures served as a control group. All specimens were stored in water at 37°C for 2 months before testing. The impact strengths (J) of the dentures were measured with a falling-weight impact test. The impact strengths of both groups were compared by a repeated measures analysis of variance (α=.05). The Weibull distribution was also applied to calculate the cumulative fracture probability as a function of impact strength. Results The mean impact strength of the control dentures was 90.0±38.1 J at crack initiation, and 95.9±37.7 J at complete fracture, whereas the impact strength of reinforced dentures was 201.7±77.9 J and 277.9±102.5 J, respectively. Statistical analysis showed that impact strength of the high-impact acrylic complete denture was significantly increased by the addition of woven E-glass fiber (P
    Original languageEnglish
    Pages (from-to)274-280
    Number of pages6
    JournalJournal of Prosthetic Dentistry
    Volume91
    Issue number3
    DOIs
    Publication statusPublished - Mar 2004

    Keywords

    • chemistry: Acrylic Resins
    • Analysis of Variance
    • chemistry: Dental Materials
    • Dental Restoration Failure
    • Denture Bases
    • Denture Design
    • Denture, Complete, Upper
    • chemistry: Glass
    • Humans
    • Materials Testing
    • Stress, Mechanical
    • Time Factors
    • chemistry: Water

    Fingerprint

    Dive into the research topics of 'The effect of reinforcement with woven E-glass fibers on the impact strength of complete dentures fabricated with high-impact acrylic resin'. Together they form a unique fingerprint.

    Cite this