Thermal degradation kinetics and decomposition mechanism of polyesters based on 2,5-furandicarboxylic acid and low molecular weight aliphatic diols

In the present work three novel alipharomatic polyesters, namely poly(ethylene 2,5-furandicarboxylate) (PEF), poly(propylene 2,5-furandicarboxylate) (PPF), and poly(butylene 2,5-furandicarboxylate) (PBF) have been prepared by applying the two-stage melt polycondensation method. The interest for polyesters prepared from renewable resources has increased recently, since they can be synthesized using monomers, like furfural or hydroxymethylfurfural and aliphatic diols. A systematic investigation of the thermal stability and decomposition kinetics of furanoate polyesters was performed using thermogravimetric analysis (TGA) and pyrolysis-gas chromatography/mass spectroscopy (Py-GC/MS). From TGA curves and activation energies it was found that PBF is less stable thermally, than the other two polyesters. The thorough studies of evolving decomposition compounds along with the isoconversional and model-fitting analysis of mass loss data led to the proposal of a decomposition mechanism for every polyester. The decomposition mechanism of 2,5-furandicarboxylate polyesters was evaluated with Py-GC/MS and from the identified decomposition products it was found that the decomposition of these polyesters is taking place mainly via β-hydrogen bond scission and in lower extent with α-hydrogen scission. 2,5-Furandicarboxylic acid, furoic acid, allyl-and diallyl-compounds are produced in the first case while aldehydes in the second. Radical decomposition also takes place producing carbonyl compounds.